3D Blend PA Nylon-Like Resin (Black, 500g)

Description

3D Blend PA Nylon-Like Resin mimics the toughness of nylon (polyamide): parts bend before they break and survive repeated assembly.

It is built for functional parts — snap fits, clips, hinges, gears and brackets — that would crack in a standard resin.

Key features

• Tough and ductile — bends before breaking
• Impact resistant
• Snap-fit friendly — survives repeated assembly
• Low water uptake compared with real nylon

Applications

• Snap fits, clips and living hinges
• Gears, bushings and wear parts
• Jigs, fixtures and brackets
• Functional prototypes of injection-moulded nylon parts

Product information

Item	Detail
Product	3D Blend PA Nylon-Like Resin
Type	PA (nylon-like) engineering resin
Colour	Black
Net weight	500 g
Wavelength	385–405 nm
Compatible printers	LCD, MSLA and DLP resin printers (Elegoo, Anycubic, Phrozen, Creality, Uniformation, Bambu and others)

Technical data

Property	Value
Tensile strength	35–40 MPa
Elongation at break	15–40%
Notched Izod impact	20–85 J/m
Density	1.05–1.25 g/cm³

Typical values for this resin type, compiled from comparable resins — indicative only, not a guaranteed specification for this batch.

How to print

1. Bring resin and room to 20–30 °C — cold resin is thick and causes failed prints
2. Shake the bottle for 1–2 minutes (or roll it) until no sediment remains
3. Check the FEP/ACF film for holes and clean the build plate; level the plate if needed
4. Pour resin into the vat up to the MAX line
5. In your slicer (Chitubox, Lychee, etc.) enter the print settings below, orient parts at 30–45° and add supports
6. Hollow large models (2–3 mm wall) and add drain holes to save resin and avoid suction
7. Run an exposure test (e.g. RERF or validation matrix) the first time you use this resin on your printer
8. Print, then let the plate drip for 10–15 min before removing parts

Recommended print settings (UV exposure)

Setting	Starting value
Layer height	0.05 mm
Bottom layers	4–6
Lift distance	8 mm
Lift speed	60–80 mm/min
Retract speed	150 mm/min
Wavelength	385–410 nm
Bottom exposure	25–35 s
Layer exposure	3–4 s

Starting values tested on a 6.6″ mono LCD (3500–4500 µW/cm²). Adjust for your printer’s light power: a stronger screen needs shorter exposure; a weaker or ageing screen needs longer.

Washing

1. Remove the build plate and let excess resin drip back into the vat (10–15 min)
2. Wash in IPA (95%+) for 2–3 min, then in a second, cleaner IPA bath for 1–2 min — do not exceed 10 min in total
3. Remove supports while the part is still slightly soft for cleaner marks
4. Dry completely with compressed air or leave 15–30 min — curing a wet part causes white haze

UV post-curing (polymerization)

Parameter	Value
Wavelength	405 nm
High-power curing box (≈200 mW/cm²)	2–3 min per side, in water
Standard curing station (40–60 W)	5–10 min, rotating
Thermal post-cure (optional)	1 h at 60–80 °C for maximum toughness

Storage & safety

• Store sealed in the original bottle at 15–30 °C, away from sunlight, heat sources and moisture
• Shake or roll the bottle for 1–2 minutes before every print — pigments and fillers settle
• Shelf life: 24 months unopened (18 months for dental resins)
• Wear nitrile gloves and safety glasses; work in a ventilated room
• Skin contact: wash with soap and water. Eye contact: rinse 15 min and seek medical advice
• Dispose of uncured resin and contaminated IPA as chemical waste, never in the drain

In the box

1 × 3D Blend PA Nylon-Like Resin (Black), 500 g bottle.