This product has the following characteristics:

  • Environmental, bio-based
  • High strength and toughness, balanced performance
  • High precision, high resolution
  • Compatible with color screen, monochrome screen, large and small size printers

This product has excellent resolution and is suitable for making props and dental models that require high resolution.

All levels (5 levels of score):

Strength (S)

3

Toughness (F)

3.5

Forming(P)

4

Accuracy (S)

4.5

Speed(A)

3

 

Performance parameters:

3D PRINTING PHOTOPOLYMER RESIN

eResin-PLA Pro

Tensile Strength(MPa)

37-48

Flexural Strength(Mpa)

36-49

Elongation at Break(%)

25-28%

     IZOD Impact Strength/(J/m)

32-36

Hardness(Shore D)

78-80

Viscosity

200-300

Density

1.09-1.10

 

Printing parameters:

eResin-PLA Recommended Settings For Printer
Exposure Time(s) Bottom Exposure Time(s) Layer Height(mm) Bottom Layer Height(mm) Lift Distence(mm) Bottom Lift Distence(mm) Retract Distence(mm) Bottom Retract Distence(mm) Lift Speed(mm/min) Bottom Lift Speed(mm/min) Retract Speed(mm/min) Bottom Retract Speed(mm/min)
ELEGOO Saturn 4,2 33 0,05 5 7 7 7 7 70 70 210 210
ELEGOO Mars 2 Pro 4 35 0,05 5 5 5 5 5 80 60 210 210
ANYCUBIC Photon Mono X 1,7 22 0,05 6 8 8 8 8 180 180 240 240
ANYCUBIC Photon Mono 4K 4 40 0,05 6 6 / 6 / 240 / 360 /
ANYCUBIC Photon Mono SE 4 35 0,05 6 6 6 6 6 240 240 240 240
VOXELAB Proxima 8.9 3,7 40 0,05 5 8 8 8 8 60 60 150 150
PHROZEN Sonic Mighty 4K 4,2 40 0,05 6 8 8 8 8 60 60 150 150
CREALITY HALOT ONE 5 40 0,05 10 6 / 6 / 60 / 60 /
CREALITY LD006 3 22 0,05 5 7 7 7 7 70 70 150 150

 

 